Notes on thermometric artefacts by Er3+ luminescence band interference

in: Journal of Luminescence (2021)
Rühl, Philipp; Wang, Dongni; Garwe, Frank; Müller, Robert; Haase, Markus; Krämer, Karl W.; Paa, Wolfgang; Heintzmann, Rainer; Heinemann, Stefan H.; Stafast, Herbert
Optical thermometry based on the intensity ratio of the 2H11/2 → 4I15/2 (525 nm) and 4S3/2 → 4I15/2 (545 nm) emission of Er3+ provides a powerful tool for microscale temperature sensing. Crystalline β-NaYF4:Er,Yb is an excellent thermometry material for green upconversion emission upon NIR laser excitation. However, interfering 2H9/2 → 4I13/2 emission is observed around 555 nm for continuous-wave laser excitation intensities above 10 W/ cm2. In this study, the green Er3+ emission bands are characterized and it is demonstrated how the true sample temperature is determined circumventing possible artefacts.

Cookies & Skripte von Drittanbietern

Diese Website verwendet Cookies. Für eine optimale Performance, eine reibungslose Verwendung sozialer Medien und aus Werbezwecken empfiehlt es sich, der Verwendung von Cookies & Skripten durch Drittanbieter zuzustimmen. Dafür werden möglicherweise Informationen zu Ihrer Verwendung der Website von Drittanbietern für soziale Medien, Werbung und Analysen weitergegeben.
Weitere Informationen finden Sie unter Datenschutz und im Impressum.
Welchen Cookies & Skripten und der damit verbundenen Verarbeitung Ihrer persönlichen Daten stimmen Sie zu?

Sie können Ihre Einstellungen jederzeit unter Datenschutz ändern.