Synthesis, characterization and optical properties of ytterbium (III) orthophosphates and their incorporation in different glass matrices

in: Journal of Physical Chemistry C (2021)
Veber, A.; Matthes, Anne; Müller, Robert; Wondraczek, Katrin; Petit, Laeticia; Salminen, Turkka
Nanosized hydrated YbPO4•nH2O powders were prepared by precipitation from aqueous solutions. It is shown that the structure, optical properties, and size of the raw particles can be further tailored by the subsequent calcination. The raw hydrous crystals transform into the anhydrous YbPO4 xenotime form after calcination at temperatures above 800 °C. In comparison with the hydrous form, the latter is characterized by a well-defined defect-free xenotime structure and multiple sharp peaks in the absorption and emission bands due to the splitting of Yb3+ 2F7/2 and 2F5/2 manifolds into multiple Stark sublevels as well as by a significant increase in the near-infrared photoluminescence intensity. It is demonstrated that the synthesized YbPO4 phosphors can withstand the corrosive behavior of phosphate glass melts; their reaction with silica glass at temperatures up to 2000 °C is negligible, and thus, YbPO4 particles can be used to prepare translucent glass−crystal composites.

Cookies & Skripte von Drittanbietern

Diese Website verwendet Cookies. Für eine optimale Performance, eine reibungslose Verwendung sozialer Medien und aus Werbezwecken empfiehlt es sich, der Verwendung von Cookies & Skripten durch Drittanbieter zuzustimmen. Dafür werden möglicherweise Informationen zu Ihrer Verwendung der Website von Drittanbietern für soziale Medien, Werbung und Analysen weitergegeben.
Weitere Informationen finden Sie unter Datenschutz und im Impressum.
Welchen Cookies & Skripten und der damit verbundenen Verarbeitung Ihrer persönlichen Daten stimmen Sie zu?

Sie können Ihre Einstellungen jederzeit unter Datenschutz ändern.