In this paper we report on an alternative technique for the preparation of ytterbium (Yb)doped silica fibers and their characteristics compared to the conventional modified chemical vapor deposition (MCVD) process in combination with solution doping and powder sinter technology (REPUSIL). In the case of the technique applied here, the active core diameter in the preform can be significantly increased via the deposition of Yb and the most important codopant, aluminum (Al), in the gas phase through the high- temperature evaporation of the Yb chelate compound and Al chloride in the MCVD process. The prepared preform shows a homogenous distribution of the refractive index and dopant concentration. The background loss of the drawn fiber was measured to be 25 dB km-1 at 1200 nm. Efficient lasing up to 200 W, showing a slope efficiency of about 80%, was demonstrated, which is comparable to fibers made via MCVD/solution doping and the REPUSIL technique.