Evaluation of light trapping structures for liquid-phase crystallized silicon on glass (LPCSG)

in: Physica Status Solidi A-Applications and Materials Science (2017)
Vetter, Michael; Jia, Guobin; Sanei, Azade; Gawlik, Annett; Plentz, Jonathan; Andrä, Gudrun
Liquid-phase crystallized silicon on glass (LPCSG) presents a promising material to fabricate high quality silicon thin films, e.g. for solar cells and modules. Using continuous wave line focus laser irradiation at 808 nm, about 10 um thick microcrystalline silicon layers are fabricated by liquid-phase crystallization of amorphous or nanocrystalline silicon layers deposited by electron beam evaporation on Borofloat 33 glass. To achieve high solar cell efficiencies with such thin silicon layers effective light trapping structures at the silicon surface are needed to enhance the light absorption and thereby the current in the solar cell. At the same time, these surface structures must provide low surface recombination velocity to maintain high open circuit voltage (Voc). Light trapping structures in LPCSG absorber prepared by conventional KOH texturing and by nanowire structuring of the solar cell backside are investigated. The impact of structures on short circuit current density (Isc) is determined from optical measurements. As a new approach effective carrier lifetime is measured in LPCSG absorbers using the quasi steady-state photoconductance method to determine the impact of structuring on surface recombination and implied Voc of solar cell precursors. Carrier lifetimes in the range of 300- 400 ns are measured indicating a carrier diffusion length of more than 20 um which is 2-3 times larger than the layer thickness. It is found that a slight pyramidal surface texture by KOH solution provides a high level of light trapping increasing Isc by 17-18% and maintaining high Voc (> 600 mV). Potential of current enhancement of nanowire structuring is higher (approx. 20%), but further optimization of nanowire dimensions and of surface cleaning of nanowire structures is needed to overcome higher surface recombination and resulting Voc losses.

Third party cookies & scripts

This site uses cookies. For optimal performance, smooth social media and promotional use, it is recommended that you agree to third party cookies and scripts. This may involve sharing information about your use of the third-party social media, advertising and analytics website.
For more information, see privacy policy and imprint.
Which cookies & scripts and the associated processing of your personal data do you agree with?

You can change your preferences anytime by visiting privacy policy.