Extruded suspended core fibers from lanthanum-aluminum-silicate glass

in: Optical Materials Express (2021)
Litzkendorf, Doris; Matthes, Anne; Schwuchow, Anka; Dellith, Jan; Wondraczek, Katrin; Ebendorff-Heidepriem, Heike
We report the use of the extrusion technique at highest temperatures to date (975 °C -1000 °C) for the fabrication of suspended core fibers (SCFs) from glass with molar composition 65 SiO2-20 Al2O3-15 La2O3 (SAL65). Through adjusting die design and fabrication conditions, extruded preforms for fibers with two different core sizes (1.2 μm and 3.1 μm) were successfully produced. Cross-sectional microstructure and material loss of these fibers highlight the potential of the extrusion technique for fabrication of microstructured optical fibers from glasses with high softening temperature and thus high thermal and mechanical stability.

Cookies & Skripte von Drittanbietern

Diese Website verwendet Cookies. Für eine optimale Performance, eine reibungslose Verwendung sozialer Medien und aus Werbezwecken empfiehlt es sich, der Verwendung von Cookies & Skripten durch Drittanbieter zuzustimmen. Dafür werden möglicherweise Informationen zu Ihrer Verwendung der Website von Drittanbietern für soziale Medien, Werbung und Analysen weitergegeben.
Weitere Informationen finden Sie unter Datenschutz und im Impressum.
Welchen Cookies & Skripten und der damit verbundenen Verarbeitung Ihrer persönlichen Daten stimmen Sie zu?

Sie können Ihre Einstellungen jederzeit unter Datenschutz ändern.