Tunable large field magnetoconductance of ZnO, ZnMnO, and ZnCoO thin films

in: Journal of Applied Physics (2019)
Vegesna, Sahitya V.; Bürger, Danilo; Patra, Rajkumar; Dellith, Jan; Abendroth, Barbara; Skorupa, Ilona; Schmidt, Oliver G.; Schmidt, Heidemarie
Magnetoconductivity of ten ZnO, Zn1_xCoxO, and Zn1_xMnxO thin films with nominal concentrations of 2.0 at.% and 0.1 at.% of Co2þ and Mn2þ ions, respectively, has been analyzed in the temperature range from 5 K to 200 K in in-plane and out-of-plane magnetic fields up to 6 T. The formation of a highly conducting surface layer can be controlled during thin film deposition, leading to a large variation of the sheet resistance, namely, from 2 _ 103 Ω/A to 1 _ 105 Ω/A at room temperature. Depending on the thickness of the highly conducting surface layer, a single two-dimensional (2D), a single three-dimensional (3D), or a two-dimensional and three-dimensional (2D + 3D) parallel conducting model was chosen to analyze the measured magnetoconductivity of the magnetic ZnO thin films with different electron spins (S ¼ 5=2 for Zn1_xMnxO and S ¼ 3=2 for Zn1_xCoxO) and with different Landé g-factors (isotropic for 3D Zn1_xMnxO and 2D Zn1_xCoxO and anisotropic for 2D Zn1_xMnxO and 3D Zn1_xCoxO).

Cookies & Skripte von Drittanbietern

Diese Website verwendet Cookies. Für eine optimale Performance, eine reibungslose Verwendung sozialer Medien und aus Werbezwecken empfiehlt es sich, der Verwendung von Cookies & Skripten durch Drittanbieter zuzustimmen. Dafür werden möglicherweise Informationen zu Ihrer Verwendung der Website von Drittanbietern für soziale Medien, Werbung und Analysen weitergegeben.
Weitere Informationen finden Sie unter Datenschutz und im Impressum.
Welchen Cookies & Skripten und der damit verbundenen Verarbeitung Ihrer persönlichen Daten stimmen Sie zu?

Sie können Ihre Einstellungen jederzeit unter Datenschutz ändern.